Punching and flanging of Metal Stamping parts are generally prepared for the next step of tapping or other processes. In general process flanging and turning holas, a series of problems such as cracking, burrs and deformation often occurre. How should stamping factories handle them in stamping processing?

1. Partes metallis pulsavi sunt holas fractas.

Haec fenomena in intersectione prima occurrit, cum punctibus concentratis, fertilibus simplicis, et etiam ab materio tabuli influentur. Therefore, it is advocatum to use materials with good stretching function and thin thickness, and to increase the aperture as much as possible during planning, which can help reduce the phenomenon of flipping holes and cracking. Convex mola plantante, elige curvaturam sphericam, adite area tangentem, cambiate direction ante foveam et pulsere foveam, convertere positivam foveam positivam et reduce fracturam.

2. Shorten the hole opening of metal stamping parts.

Aperimenti irregulari fluctus difficile facient fluctum. Analizantes rationes, invenietis quod gapus inter concave et convex molda est fonte problemae, causantes materiae reboundi. Praeceptum standard est adigurare gapum molda ad paululum minus quam densitatem materiae ut verticalem aspicientem per stampionem assegurat. 3. Insufficient flipping height of metal stamping parts.

Insufficient a altitudo cavernis facile potest inducere ad phenomenum succidentium angulorum, subcutorem profunditatem fluminantium scilorum, et influentem functionem ligaminis. Pro hoc, precision metalla stamping processing factories qui longo cooperantur facie probationem, crescere altitudinem cavernis in tempore, aut tenere parietem densitatem cavernis ut cresceret altitudinem cavernis.

4. Rotatio radius metalorum partibus non correspondit.

Si radius foraminis nimis magnus est, effectabit coniunctionem apparentis et scintis, dissolvens produktum congregatum, et proba fidelitatis non transibit. Analizantes rationes, principes causae sunt anguli rotundae molae concavei intrinsecus et densitatem materiae. Quanto maior est densitatem, maior radius, et maior anguli rotundae molae concavei, maior radius. So choosing to expose and reduce the rounded corners of the imported material can solve the problem. Maybe when the material is thicker, a planning and shaping shoulder can be recruited to modify the radius.

5. Struktura stampionis metallis moritur non correspondit.

A causa malligationis structurae molae et damnationis materiae facile est materiae fragere et saltare in groveam causantem phenomenum punctionis et dissipationis solitudinis. The negative impact is that it will cause unevency on the surface of the product, resulting in defective products, making after-sales processing difficult and consuming manpower and resources.

This article is from EMAR Mold Co., Ltd. For more EMAR related information, please click: www.sjt-ic.com，